TítuloAdhesion characterization of tungsten mine waste geopolymeric binder. Influence of OPC concrete substance surface treatment
Autor(es)Torgal, Fernando Pacheco
Gomes, J. P. Castro
Jalali, Said
Palavras-chaveGeopolymeric binder
Mine waste
Repair products
Bond strength
Data2008
EditoraElsevier
RevistaConstruction and Building Materials
Citação"Construction and Building Materials". ISSN 0950-0618 (2008) 154-161.
Resumo(s)Tungsten mine waste mud (TMWM) was investigated for its potential use as repair material of ordinary portland cement (OPC) concrete. Bond strength between OPC concrete substrate and three repair materials was analysed. TMWM geopolymeric binder and two commercial repair products were used as repair materials. Bond strength behaviour was assessed from slant shear tests. A total of 128 slant shear specimens were made in order to evaluate bond strength at 1, 3, 7 and 28 days curing. Four kinds of concrete substrate surface treatment were used, as cast against metallic formwork, as cast against wood formwork, saw cut and acid etching. This study indicates that TMWM geopolymeric binders possess very high bond strength even at early ages and that behaviour is not affected by low surface treatment roughness. Commercial repair products on the other hand show very low bond strength and are very dependent on surface treatment roughness. Scanning electron micrographs reveal that TMWM geopolymeric binders chemically bond to the concrete substrate, while cost comparisons show this geopolymeric repair solution is by far the most cost efficient.
Tipoarticle
URIhttp://hdl.handle.net/1822/7155
ISSN0950-0618
Versão da editorawww.elsevier.com/locate/conbuildmat
Arbitragem científicayes
AcessoopenAccess
Aparece nas coleções:C-TAC - Artigos em Revistas Internacionais

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
Torgal_RI_4_2008.pdf902,48 kBAdobe PDFVer/Abrir

Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu Currículo DeGóis