dc.contributor.advisorVaz, F.-
dc.contributor.advisorCunha, L.-
dc.contributor.authorCarvalho, Miguel Ângelo Mendes da Costapor
dc.date.accessioned2015-03-31T10:47:19Z-
dc.date.available2015-03-31T10:47:19Z-
dc.date.issued2014-
dc.date.submitted2014-
dc.identifier.urihttps://hdl.handle.net/1822/34646-
dc.descriptionDissertação de mestrado em Ciências – Formação Contínua de Professores (área de especialização em Física e Química)por
dc.description.abstractEste projeto insere-se numa das linhas de investigação do Grupo de Revestimentos Funcionais (GRF) que tem como objetivo o estudo de propriedades de filmes finos para diversas aplicações óticas. No âmbito desta proposta de tese, pretende-se dar seguimento a um projeto de investigação aprovado pela Fundação para a Ciência e Tecnologia. Produziram-se diversos filmes finos de TiO2(Au) e TiO2 (Ag), usando a técnica de pulverização catódica reativa em magnetrão, com alimentações de corrente contínua, CC. Para se produzir os filmes referidos, utilizou-se um alvo de titânio com 99.9 % de pureza, onde se colocaram pequenos pedaços de ouro ou de prata na superfície do referido alvo. Seguidamente, fez-se a caracterização dos filmes através das técnicas de espectrometria de retrodispersão de Rutherford (RBS) (composição química), difração de raios-X (XRD) (estrutura cristalina) e microscopia eletrónica de varrimento (SEM) (morfologia e espessura), bem como dos coeficientes óticos (transmitância e refletância). Para determinar a resistividade elétrica dos filmes finos produzidos, utilizou-se o método das 4 pontas para as amostras condutoras e o método das 2 pontas para as amostras isoladoras. Finalmente, colocou-se os filmes finos em banhos de suor artificial a diferentes durações, para estudar de que modo a duração e o suor artificial alteram os coeficientes óticos e a resistividade elétrica.por
dc.description.abstractThis project belongs to one of the lines of research of the Functional Coatings Group (GRF) that aims to study the properties of thin films for various optical applications. Within this thesis proposal, it is intended to continue a research project approved by the Foundation for Science and Technology. Were produced several TiO2 (Au) and TiO2(Ag) thin films, using the technique of reactive magnetron sputtering, with current power sources, DC. To produce such films, it was used a titanium target with 99.9 % purity, where were placed small pieces of gold or silver on the surface of the referred target. Then, it was made the characterization of the films by Rutherford backscattering Spectrometry (RBS) (chemical composition), X-ray diffraction (XRD) (crystal structure) and scanning electron microscopy (SEM) (morphology and thickness) techniques as well as of the respective optical coefficients (transmittance and reflectance). To determine the electrical resistivity of the thin films produced, it was used the four-point probe method for the conductive samples and the two-point probe method for the insulating samples. Finally, the thin films were placed in artificial sweat baths at different durations, to study how the duration and the artificial sweat alter the optical coefficients and the electrical resistivity.por
dc.language.isoporpor
dc.rightsopenAccesspor
dc.subjectPulverização catódica em magnetrãopor
dc.subjectNanopartículas de ouropor
dc.subjectResistividadepor
dc.subjectMétodo das 4 pontaspor
dc.subjectMétodo das 2 pontaspor
dc.subjectSuor artificialpor
dc.subjectMagnetron sputteringpor
dc.subjectGold nanoparticlespor
dc.subjectResistivitypor
dc.subjectFour-point probe methodpor
dc.subjectTwo-point probe methodpor
dc.subjectArtificial sweatpor
dc.titleProdução e caracterização de filmes finos de TiO2(Au) e TiO2(Ag) para aplicações biomédicaspor
dc.typemasterThesispor
dc.subject.udc538.975por
dc.identifier.tid201348411por
sdum.uoeiEscola de Ciênciaspor
dc.subject.fosCiências Naturais::Ciências Físicaspor
Aparece nas coleções:BUM - Dissertações de Mestrado
CDF - ENSINO - Dissertações de Mestrado/Master Thesis

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
Miguel Ângelo Mendes da Costa Carvalho.pdf3,68 MBAdobe PDFVer/Abrir

Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu ORCID