Título: | Desgaste de materiais dentários de restauro direto |
Outro(s) título(s): | Wear of dental materials on direct restoration |
Autor(es): | Bentes, Ana Catarina Fernandes |
Orientador(es): | Gomes, J. R. Souza, J. C. M. |
Data: | 2014 |
Resumo(s): | O desenvolvimento de resinas compostas como materiais de restauro dentário direto surgiu através da necessidade de materiais com características óticas semelhantes à estrutura dentária natural. Contudo, o desgaste destas resinas persiste como um dos principais problemas clínicos. Através de vários estudos, verificou-se que a resistência ao desgaste destes materiais depende fundamentalmente de aspetos relacionados com as partículas de carga, nomeadamente do seu tamanho e distribuição, assim como a sua percentagem volumétrica.
O principal objetivo do presente trabalho consistiu na caracterização tribológica de resinas compostas de restauro dentário através da avaliação da sua resistência ao desgaste abrasivo e de deslizamento e pela identificação dos mecanismos de desgaste dominantes. Testes de compressão permitiram determinar a resistência à compressão das resinas compostas assim como o seu módulo de elasticidade. Foram efetuados testes de ball cratering utilizando uma emulsão à base de pasta dentífrica Colgate®Anti-tártaro mais branqueamento como abrasivo, com uma carga normal aplicada de 3 N e uma duração de 300 rotações. O estudo de caracterização tribológica foi complementado com testes de deslizamento linear alternativo na geometria esfera-placa em presença de saliva artificial à temperatura de 37 °. O deslizamento ocorreu contra alumina, com frequência de 1 Hz e carga normal de 25 N.
Foi avaliado o volume de desgaste dos diferentes grupos de resinas compostas em estudo o qual foi relacionado com as suas propriedades mecânicas e a composição em termos de tamanho e percentagem volumétrica das partículas de carga. Como principal conclusão destaca-se a confirmação do papel determinante das partículas de carga no comportamento tribológico das resinas compostas, seja em consequência da ação abrasiva de uma pasta dentífrica, seja como resultado do deslizamento contra uma superfície cerâmica. The development of composite resins as dental restoration materials came through the need for materials that were similar to natural tooth structure. However, wear of these resins still remains as a major clinical problem. Through various conducted studies, it was found that the wear resistance of these materials mainly depends on aspects related with the filler particles, in particular their size and distribution as well as its volume percentage. The main objective of this work was the tribological characterization of composite resins for direct dental restoration by the evaluation of their resistance to abrasive and sliding wear as well as by the identification of the dominant wear mechanisms. Compression tests have allowed to determine the compressive strength of the composites as well as their modulus of elasticity. Micro-abrasion tests using slurry based on Colgate®Anti-tartar toothpaste whitening as abrasive, with a normal applied load of 3 N and lasting for 300 revolutions were made. The tribological characterization was complemented by reciprocating sliding wear tests using a ball-on-plate geometry in the presence of artificial saliva, at 37° C. Alumina was used as counterface material and these tests were carried out at constant a frequency of 1 Hz and normal applied load of 25 N. The wear volume was evaluated for the different groups of composite resins and correlated with their mechanical properties and composition in terms of size and volume percentage of filler particles. The determinant role of filler particles on the tribological behavior of composite resins was confirmed both as a consequence of the abrasive action of a toothpaste or due to the sliding against a ceramic surface. |
Tipo: | Dissertação de mestrado |
Descrição: | Dissertação de mestrado integrado em Engenharia Biomédica (área de especialização em Biomateriais, Reabilitação e Biomecânica) |
URI: | https://hdl.handle.net/1822/34485 |
Acesso: | Acesso aberto |
Aparece nas coleções: | BUM - Dissertações de Mestrado |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Desgaste de Materiais Dentários de Restauro Direto.pdf | 2,85 MB | Adobe PDF | Ver/Abrir |