TítuloAg-Ti(C,N)-based coatings for biomedical applications : influence of silver content on the structural properties
Autor(es)Manninen, N. K.
Galindo, R. Escobar
Benito, N.
Figueiredo, N. M.
Cavaleiro, A.
Palacio, C.
Carvalho, S.
EditoraIOP Publishing
RevistaJournal of Physics D: Applied Physics
Resumo(s)Ag–TiCN coatings were deposited by dc reactive magnetron sputtering and their structural and morphological properties were evaluated. Compositional analysis showed the existence of Ag–TiCN coatings with different Ag/Ti atomic ratios (ranging from 0 to 1.49). The structural and morphological properties are well correlated with the evolution of Ag/Ti atomic ratio. For the samples with low Ag/Ti atomic ratio (below 0.20) the coatings crystallize in a B1-NaCl crystal structure typical of TiC0.3N0.7. The increase in Ag/Ti atomic ratio promoted the formation of Ag crystalline phases as well as amorphous CNx phases detected in both x-ray photoelectron spectroscopy and Raman spectroscopy analysis. Simultaneously to the formation of Ag crystalline phases and amorphous carbon-based phases, a decrease in TiC0.3N0.7 grain size was observed as well as the densification of coatings.
Arbitragem científicayes
Aparece nas coleções:CDF - GRF - Artigos/Papers (with refereeing)

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
Ag–Ti(C, N)-based coatings for.pdf2,28 MBAdobe PDFVer/Abrir

Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu Currículo DeGóis