TítuloAluminum-free glass-ionomer bone cements with enhanced bioactivity and biodegradability
Autor(es)Gomes, Filipa Oliveira
Pires, R. A.
Reis, R. L.
Palavras-chaveBioactive
Biodegradable
Bone cements
Glass-ionomer cements
Mechanical Properties
DataAbr-2013
EditoraElsevier
RevistaMaterials Science and Engineering: C
Resumo(s)Al-free glasses of general composition 0.340SiO2:0.300ZnO:(0.250-a-b)CaO:aSrO:bMgO:0.050Na2O:0.060P2O5 (a, b=0.000 or 0.125) were synthesized by melt quenching and their ability to form glass-ionomer cements was evaluated using poly(acrylic acid) andwater.We evaluated the influence of the poly(acrylic acid)molecular weight and glass particle size in the cementmechanical performance.Higher compressive strength (25±5 MPa) and higher compressive elasticmodulus (492±17 MPa) were achieved with a poly(acrylic acid) of 50 kDa and glass particle sizes between 63 and 125 μm. Cements prepared with glass formulation a=0.125 and b=0.000 were analyzed after immersion in simulated body fluid; they presented a surface morphology consistent with a calcium phosphate coating and a Ca/P ratio of 1.55 (similar to calcium-deficient hydroxyapatite). Addition of starch to the cement formulation induced partial degradability after 8 weeks of immersion in phosphate buffer saline containing α-amylase. Micro-computed tomography analysis revealed that the inclusion of starch increased the cement porosity from 35% to 42%. We were able to produce partially degradable Al-free glass-ionomer bone cements with mechanical performance, bioactivity and biodegradability suitable to be applied on non-load bearing sites and with the appropriate physical characteristics for osteointegration upon partial degradation. Zn release studies (concentrations between 413 μM and 887 μM) evidenced the necessity to tune the cement formulations to reduce the Zn concentration in the surrounding environment.
Tipoarticle
URIhttp://hdl.handle.net/1822/23279
DOI10.1016/j.msec.2012.12.037
ISSN0928-4931
Versão da editorahttp://www.sciencedirect.com/science/article/pii/S0928493112005942
Arbitragem científicayes
AcessorestrictedAccess
Aparece nas coleções:3B’s - Artigos em revistas/Papers in scientific journals

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
Materials Science and Engineering C, 33 (2013), 1361-1370.pdf1,32 MBAdobe PDFVer/Abrir  Solicitar cópia ao autor!

Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu Currículo DeGóis