Título: | Efeito do envelhecimento acelerado sobre as propriedades de microconcreto reforçado com fibras longas de sisal |
Outro(s) título(s): | Effect of accelerated aging on the properties of microconcrete reinforced with sisal fibers |
Autor(es): | Lima, Paulo Roberto Lopes Toledo Filho, Romildo Dias Neumann, Reiner Barros, Joaquim A. O. |
Palavras-chave: | Compósitos Envelhecimento acelerado Durabilidade Composite Accelerated aged Durability |
Data: | 2019 |
Editora: | Associação Nacional de Tecnologia do Ambiente Construído (ANTAC) |
Revista: | Ambiente Construído |
Citação: | Lima, P. R. L., Toledo Filho, R. D., Neumann, R., & Barros, J. A. O. (2019). Efeito do envelhecimento acelerado sobre as propriedades de microconcreto reforçado com fibras longas de sisal. Ambiente Construído, 19(1), 7-20 |
Resumo(s): | Neste trabalho dois microconcretos, com e sem metacaulinita, foram
dosados para produção de compósitos laminados reforçados com
fibras longas de sisal. Para garantir uma matriz livre de hidróxido de
cálcio foi determinado o teor ideal de metacaolinita por análise
termogravimétrica de pastas com teores de substituição de 20%, 30% e 40 nas
idades de 4 h, 10 h, 24 h, 7 dias, 28 dias e 730 dias. Laminados com 30% de
metacaolinita foram submetidos a ensaio de flexão após 28 dias de cura em água e
após 12 e 25 ciclos de molhagem e secagem. A análise da microestrutura foi
realizada a partir de microscopia eletrônica de varredura e espectroscopia de raios
X por energia dispersiva (EDS). Os resultados demonstram que, no microconcreto
contendo apenas cimento, o hidróxido de cálcio foi lixiviado da matriz e
depositado na superfície da fibra, o que resultou em ruptura brusca devido ao
enfraquecimento das fibras. Com a adição de metacaolinita, a matriz mostrou-se
livre de hidróxido de cálcio, e o comportamento mecânico pós-fissuração não foi
alterado pelo envelhecimento. No entanto, a variação de temperatura e umidade do
ciclo molhagem-secagem induziu fissuração do microconcreto, o que
negativamente afetou a resistência à formação da primeira fissura do compósito e
seu modo de ruptura In this study, two microconcrete samples, with and without metakaolin, were designed for the production of laminated composites reinforced with long sisal fibres. In addition to the reference microconcrete, another microconcrete was produced by replacing cement by metakaolin.The ideal metacaolin content that would guarantee a free calcium hydroxide matrix was determined by thermogravimetric analysis of blends with 20%, 30% and 40% substitution contents at the ages of 4 h, 10 h, 24 h, 7 days, 28 days and 730 days. Laminates produced with cement substitution by 30% metakaolin were submitted to flexural test after 28 days of curing in water, and after 12 and 25 wetting and drying cycles. The analysis of the microstructure was performed by scanning electron microscopy and dispersive energy X-ray spectroscopy (EDS). The results demonstrate that in the microconcrete containing only cement, the calcium hydroxide was leached from the matrix and deposited on the surface of the fibre. Thus, the aged composites showed a sudden rupture due to the weakening of the fibres. With the incorporation of metakaolin, the matrix showed to be free of calcium hydroxide, and the mechanical behaviour after cracking was not altered by aging. However, the temperature and humidity variation due the wet-drying cycle has induced cracking of the microconcrete, which detrimentally affected the strength at crack initiation of these composites and their rupture mode |
Tipo: | Artigo |
URI: | https://hdl.handle.net/1822/72292 |
DOI: | 10.1590/s1678-86212019000100289 |
ISSN: | 1415-8876 |
e-ISSN: | 1678-8621 |
Versão da editora: | https://www.scielo.br/scielo.php?pid=S1678-86212019000100007&script=sci_arttext&tlng=pt |