Characterization of intermediate stages in the precipitation of hydroxyapatite at 37°C

Abstract

Precipitation of hydroxyapatite Ca 5(PO 4) 3OH (HAp) was carried out by mixing a saturated calcium hydroxide aqueous solution with an orthophosphoric acid aqueous solution at 37°C. In order to promote optimal conditions for the production of HAp with high yields, mixing of the reaction medium was assured by a novel metal stirrer. Different experimental conditions were studied varying the mixing Ca/P molar ratio from 1 to 1.67. After process optimization, a suspension of HAp particles with pH close to 7 was obtained for a mixing molar ratio Ca/P=1.33. The precipitation process was then characterized as a function of pH and calcium concentration, revealing the existence of three different stages. The precipitate formed in each stage was characterized by scanning electron microscopy and X-ray diffraction.