TítuloExperimental analysis of the carbonation and humidity diffusion processes in aerial lime mortar
Autor(es)Oliveira, Mateus António Nogueira
Azenha, Miguel
Lourenço, Paulo B.
Meneghini, A.
Guimarães, Erika Tinoco
Castro, Fernando
Soares, Delfim
Palavras-chaveAerial lime
Mortar
Carbonation
Thermogravimetric analysis
Humidity diffusion process
Phenolphthalein
Compressive strength
Data2017
EditoraElsevier
RevistaConstruction and Building Materials
Resumo(s)Aerial lime has been commonly used as binder for preparing mortar in masonry constructions for centuries. Knowledge about the material behaviour of aerial lime is however still limited, and contributions are necessary for better understanding of the evolution of its physical and mechanical properties, in particular concerning the structural behaviour of both historical and new constructions comprising of aerial lime. In this work, an experimental program was developed in order to study aerial lime mortars, specifically addressing the drying and carbonation processes. Regarding the measurement of drying process, the humidity diffusion was monitored in one-dimensional flux conditions. The phenomena associated with self-desiccation were also investigated. For evaluation of the carbonation process, different cylindrical specimens have been studied with phenolphthalein indicator and thermogravimetric analyses. In order to exclusively investigate the carbonation reaction, without the effect of internal humidity gradients in the tested specimens, thin discs of mortar were tested. Also, the compressive strength evolution was analysed using cubic specimens. The most relevant findings can be summarized as following: (i) humidity diffusion was quicker than normally observed in cement-based materials; (ii) a strong effect of the size of specimens has been observed in early ages (before 10 days), which became negligible as time progressed; (iii) up to 70% maximum carbonation was observed in TGA testing, when direct measurement of actual decarboxylation was made, as opposed to mere inference based on the dehydroxylation.
Tipoarticle
URIhttp://hdl.handle.net/1822/51529
DOI10.1016/j.conbuildmat.2017.04.120
ISSN0950-0618
e-ISSN1879-0526
Versão da editorahttps://doi.org/10.1016/j.conbuildmat.2017.04.120
Arbitragem científicayes
AcessorestrictedAccess
Aparece nas coleções:ISISE - Artigos em Revistas Internacionais

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
[45].pdf1,39 MBAdobe PDFVer/Abrir  Solicitar cópia ao autor!

Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu Currículo DeGóis