TitleInfluence of oxygen content on the antibacterial effect of Agx-Ox coatings deposited by magnetron sputtering
Author(s)Rebelo, Rita
Fangueiro, Raúl
Henriques, Mariana
Carvalho, S.
Issue date2016
Abstract(s)Ag and AgOx thin films were deposited by pulsed DC magnetron sputtering, for stents devices, in order to provide antibacterial properties. During the deposition process, oxygen flow was varied (0-15 sccm) to understand the influence of oxygen species in the physical, chemical and structural properties of thin films. Coatings morphology was observed by scanning electron microscopy (SEM) and their nanostructure and composition were assessed by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) and energy dispersive spectroscopy (EDS), respectively. XRD and XPS analyses revealed that Ag thin films are composed by metallic Ag, which crystallizes in fccAg phase; whereas AgOx showed a mixture of Ag2O and AgO phases for low oxygen fluxes that became single AgO with the increase of oxygen flow. Surface wettability and surface tension of the coatings were also determined showing hydrophobic character. Halo inhibition zone tests were performed against Staphylococcus epidermidis, in order to evaluate the antibacterial behavior of coatings, and silver ion release was measured. Only AgOx presented antibacterial behavior, showing that the presence of silver oxide are the main reasons for the antibacterial effect, probably due to the increased production of ROS (Reactive Oxygen Species), making these coatings promising for stents’ applications.
TypeConference paper
URIhttp://hdl.handle.net/1822/44415
Peer-Reviewedyes
AccessOpen access
Appears in Collections:DET/2C2T - Comunicações em congressos internacionais com arbitragem científica


Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu ORCID