Please use this identifier to cite or link to this item: http://hdl.handle.net/1822/43386

TitleFunctional behaviour of TiO2films doped with noble metals
Author(s)Rodrigues, M. S.
Borges, J.
Gabor, C.
Munteanu, D.
Apreutesei, M.
Steyer, P.
Lopes, C.
Pedrosa, P.
Alves, E.
Barradas, N. P.
Cunha, L.
Martínez-Martínez, D.
Vaz, F.
KeywordsMagnetron sputtering
Thin films
Brittleness
Noble metal doping
Titanium dioxide
Issue date2016
PublisherTaylor & Francis
JournalSurface Engineering
CitationRodrigues, M. S., Borges, J., Gabor, C., Munteanu, D., Apreutesei, M., Steyer, P., . . . Vaz, F. (2016). Functional behaviour of TiO2 films doped with noble metals. Surface Engineering, 32(8), 554-561. doi: 10.1179/1743294415y.0000000085
Abstract(s)To evaluate the effects of different concentrations of noble metal in a TiO2 matrix, different films of both Ag:TiO2 and Au:TiO2 systems were prepared. Mechanical and tribological characterization was carried out to evaluate the coatings response as a function of the noble metals composition and (micro)structure of the films. The overall set of results indicates that the amorphous films reveal better results than the crystalline ones. For the amorphous samples, the reduced Young’s modulus and the adhesion critical loads followed similar tendencies in both sets of films. Wear rates were similar for all samples except for the one with the highest silver content. To improve brittleness of TiO2 films, the results seem to indicate that a slight metal doping is preferred, and Au showed to be a better choice than Ag. In fact, the sample with the lowest Au content revealed a better mechanical behaviour than the pure TiO2 film.
Typearticle
URIhttp://hdl.handle.net/1822/43386
DOI10.1179/1743294415Y.0000000085
ISSN0267-0844
Peer-Reviewedyes
AccessopenAccess
Appears in Collections:CDF - GRF - Artigos/Papers (with refereeing)

Files in This Item:
File Description SizeFormat 
MS Rodrigues et al Surface Engineering.pdf1,04 MBAdobe PDFView/Open

Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu Currículo DeGóis