TitleIncorporation of proteins and enzymes at different stages of the preparation of calcium phosphate coatings on a degradable substrate by a biomimetic methodology
Author(s)Azevedo, Helena S.
Leonor, I. B.
Alves, C. M.
Reis, R. L.
KeywordsBiodegradable polymers
Starch
Biomaterials
Biomimetic coatings
Calcium phosphate
Enzymes and proteins incorporation
Degradation
Bone
Issue date2005
PublisherElsevier
JournalMaterials Science and Engineering: C
Citation"Materials Science and Engineering C". ISSN 0928-4931. 25:2 (2005) 169-179..
Abstract(s)In this work, the possibility of incorporating proteins into calcium phosphate (Ca-P) coatings, prepared on the surface of starch polymeric biomaterials by means of a biomimetic route, was investigated. The morphology, chemical composition and crystallinity of Ca-P coatings was assessed and related to the incorporation of the studied biomolecules. For that, bovine serum albumin (BSA) and aamylase were added in concentrations of 1 mg/ml to simulated body fluid (SBF) solutions, being both added at the nucleation or growth stages of the biomimetic coating process. A biodegradable blend of corn starch/ethylene vinyl alcohol (SEVA-C) was used as substrate and bioactive glass (45S5 BioglassR) was used as the nucleating agent. The obtained Ca-P coatings were characterised by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), Fourier transform infrared spectroscopy using an attenuated reflectance device (FTIR-ATR) and thin-film X-ray diffraction (TF-XRD). Additionally, to evaluate the activity of the incorporated enzyme and the stability of the Ca-P films, coated samples were immersed in an SBF solution for different periods of time. The enzyme activity was measured and the morphology of the coating examined by SEM. The results obtained showed that the presence of protein molecules, at the nucleation or growth stages, lead to the formation of a dense Ca-P film presenting different morphologies that were different of the selected coating conditions. FTIR-ATR analysis detected the presence of carbonate and phosphate groups on the Ca-P layer, indicating the formation of a coating similar to the mineral component of vertebrates bone tissue. When proteins were added, amide I and amide II bands, characteristic groups of protein molecules, were also detected, revealing the efficient incorporation of these biomolecules into the Ca-P coatings. Ca-P coatings, with a-amylase incorporated at the nucleation stage, showed no degradation of the film after incubation in SBF for 28 days. The release of increasing concentration of reducing sugars with degradation time revealed that a-amylase was efficiently incorporated in the coating remaining active throughout the coating preparation. This can be a strategy that will allow, in addition of conferring osteoconductive properties to biodegradable polymers, also simultaneously tailoring their degradation kinetics.
TypeArticle
URIhttp://hdl.handle.net/1822/4022
DOI10.1016/j.msec.2005.01.007
ISSN0928-4931
Peer-Reviewedyes
AccessOpen access
Appears in Collections:3B’s - Artigos em revistas/Papers in scientific journals

Files in This Item:
File Description SizeFormat 
0098.pdf536,64 kBAdobe PDFView/Open

Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu ORCID