TitleGe thin film anode in a flexible solid-state Li-ion microbattery
Author(s)Vieira, E. M. F.
Ribeiro, J. F.
Rua, João
Silva, Maria Manuela
Correia, J. H.
Goncalves, L. M.
Issue date23-Oct-2015
Abstract(s)Flexible solid-state lithium ion batteries (LIBs) have become an important part of the portable electronics due to their flexibility, lightweight, easy portability, security and the ability to be adjusted in large-scale energy storage microsystems, with significantly high power and long cycle life. Germanium (Ge) is a promising anode material for high-generation LIBs, with high theoretical capacity (1600 mAh/g corresponding to Li4.4Ge), fast Li ion diffusivity (i.e. 400 times faster than silicon) and good electronic conductivity (104 times higher than silicon) which allow high charge/discharge rates. Here, electrochemical performance of e-beam deposited Ge anode (300 nm thick) coupled with LiCoO2/LIPON (cathode/electrolyte) in a microbattery system was investigated. The battery (figure 1) was fabricated only by PVD techniques. LiCoO2 was deposited by RF-sputtering (120 W RF power; 17 sccm of Ar) and LIPON with the conditions explained in JF Ribeiro, et al. [1]. Open circuit potential (figure 2), charge/discharge cycles (figure 3) and electrochemical impedance spectroscopy (EIS), at room temperature, were performed.
TypeConference paper
URIhttp://hdl.handle.net/1822/37898
Peer-Reviewedyes
AccessRestricted access (UMinho)
Appears in Collections:CAlg - Artigos em livros de atas/Papers in proceedings
CDQuim - Comunicações e Proceedings
DEI - Artigos em atas de congressos internacionais

Files in This Item:
File Description SizeFormat 
Artigo_ElianaVieira.pdf
  Restricted access
Conference Paper572,27 kBAdobe PDFView/Open    Request a copy!

Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu ORCID