Please use this identifier to cite or link to this item: http://hdl.handle.net/1822/29690

TitleArgamassas sustentáveis de baixa retração
Author(s)Martins, Vânia
Advisor(s)Aguiar, J. L. Barroso de
Fangueiro, Raúl
KeywordsArgamassa
Sustentabilidade
Cal
Fibras
Gesso
Retração
Material de mudança de fase
Mortar
Lime
Fibers
Gipsum
Shrinkage
Phase change material
Issue date2012
Abstract(s)Os materiais de mudança de fase tendem cada vez mais a serem utilizados na construção, devido às suas propriedades de armazenamento de energia, quer de verão quer de inverno, possibilitando assim a melhoria das propriedades térmicas das edificações num período de 24 horas, sem haver necessidade de recorrer a equipamentos de climatização, contribuindo, desta forma, para um melhoramento do impacto ambiental. A introdução de fibras e gesso em argamassas de cal contribui para o melhoramento da retração, compensando o agravamento provocado pela incorporação do PCM. Assim, obtêm-se argamassas de revestimento sustentáveis devido às suas propriedades térmicas. O estudo da retração consistiu no ensaio de cinco argamassas com diferentes composições. A retração foi avaliada no estado fresco e no estado endurecido. Nas argamassas estudadas foi-se variando a percentagem de PCM, 10%, 20% e 30%, nas composições em que as argamassas fissuraram introduziu-se gesso e fibras. A argamassa com 10% de PCM, foi aquela que apresentou melhores valores de ensaios mecânicos, cujo seu aumento é cerca de 40% na resistência à flexão e de 57% na resistência à compressão, em comparação com a argamassa de referência C100G0PCM0. Das cinco composições estudadas, a argamassa cuja composição é 20% PCM, 40%Gesso e 60% de Cal, foi aquela que possui melhores valores de retração.
Phase change materials tends to be increasingly used in construction due to their energy storage properties either during summer or winter. Thus enabling the improvement of thermal properties of the building along the day without the need for air conditioning systems, contributing to reduce the environmental impact. The introduction of fibers and gypsum mortar of lime contributes to improving the shrinkage compensating the deterioration caused by the incorporation of PCM. Thus, mortar are obtained coating sustainable due to their termal properties. The study of the shrinkage consists of test five mortars with diferente compositions. The shrinkage was assessed in fresh and hardened state. In mortars was studied by varying the percentage of PCM, 10%, 20% and 30%, in compositions in which the mortar was introduced crack gypsum and fibers. The mortar with 10% PCM, was the one that showed the best values of mechanical of the test, which is its increased about 40% in the flexural strength and 57% in compressive strength, compared to the reference mortar C100G0PCM0. The mortar with 20% PCM, 40% gypsum and 60% of lime in the composition, presented the best results for shrinkage.
TypeMaster thesis
DescriptionDissertação de mestrado integrado em Engenharia Civil
URIhttp://hdl.handle.net/1822/29690
AccessOpen access
Appears in Collections:BUM - Dissertações de Mestrado Integrado
C-TAC - Dissertações de Mestrado

Files in This Item:
File Description SizeFormat 
dissertação_Vânia Martins_2012.pdf1,97 MBAdobe PDFView/Open

Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu ORCID