Please use this identifier to cite or link to this item: http://hdl.handle.net/1822/21780

TitleEstudo das propriedades mecânicas em filmes nanocompósitos multifuncionais
Author(s)Matos, João Nuno Oliveira Gomes de
Advisor(s)Gomes, J. R.
Faro, Marc Torrell
KeywordsFilmes finos
Nanocompósitos
Efeito ressonância de plasmão
Tribologia
Atrito
Desgaste
Thin films
Nanocomposits
Plasmon efect
Tribology
Friction
Wear
Issue date2011
Abstract(s)O objectivo deste trabalho consistiu em caracterizar o comportamento tribológico de filmes finos nanocompósitos com nanoparticulas de ouro dispersas numa matriz dieléctrica de óxido de titânio (TiO2). Foram efectuadas duas deposições em amostras com diferentes concentrações de ouro, sobre as quais foram efectuados recozimentos térmicos de 300 e 500ºC. Foram medidas a cor e reflectividade de cada amostra e relacionadas com a concentração de ouro e a importância para as propriedades ópticas. O principal foco incidiu sobre as variações do coeficiente de atrito, taxa de desgaste e sobre a generalidade das restantes características que resultam da modificação da morfologia dos filmes finos em função dos diferentes recozimentos efectuados em vácuo a temperaturas cada vez mais elevadas. Nestas últimas características deu-se particular interesse à formação dos aglomerado de ouro, ao aumento do tamanho de grão e da cristalização da matriz dieléctrica de óxido de titânio e a sua relação com as alterações no comportamento tribológico.
The aim of this work is to demonstrate de tribological behavior of thin film nanocomposites consisting of gold nanoparticles dispersed in a dielectric matrix of TiO2. Two series of depositions with different concentrations of gold are carried out on samples, on which are conducted thermal annealing’s at 300 and 500º C. The samples color and reflectivity were measured and related to the concentration of gold, allowing the optimization of the optical properties The main focus was given to the changes in the friction coefficient and wear rate, the overall tribological features resulting from the morphological changes induced by annealing experiments in vacuum, at increasing temperatures. In particular, the gold clustering, the increase of grain size and the crystallization of the TiO2 dielectric matrix were correlated with the changes in the tribological parameters.
TypeMaster thesis
DescriptionDissertação de mestrado integrado em Engenharia Mecânica
URIhttp://hdl.handle.net/1822/21780
AccessOpen access
Appears in Collections:BUM - Dissertações de Mestrado Integrado
DEM - Dissertações de Mestrado / MSc Thesis

Files in This Item:
File Description SizeFormat 
Tese João Matos.pdf3,72 MBAdobe PDFView/Open

Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu ORCID