TitleJoining Ti-47Al-2Cr-2Nb with a Ti/(Cu,Ni)/Ti clad-laminated braze alloy
Author(s)Guedes, A.
Pinto, A. M. P.
Vieira, M. F.
Viana, Filomena
KeywordsTiAl
Diffusion brazing
Interface
Hardness
Issue date2003
PublisherKluwer
JournalJournal of Materials Science
Citation"Journal of materials science". ISSN 0957-4530. 38 (2003) 2409-2414.
Abstract(s)The joining of Ti-47Al-2Cr-2Nb using Ti-15Cu-15Ni (wt.%) as braze alloy was investigated. Experiments were conducted at 980 and 1000ºC for 10 min. The microstructure and the chemical composition of the interfaces were studied by scanning electron microscopy (SEM) and by energy dispersive X-ray spectroscopy (EDS), respectively. For both processing conditions the reaction between the gamma-TiAl alloy and the braze alloy produced layered interfaces, which are essentially composed of apha2-Ti3Al and of Ti-Ni-Cu-Al and Ti-Ni-Cu intermetallic compounds. Microhardness tests showed that all reaction layers are harder than either the gamma or the (alpha2 + gamma) lamellar grains of the intermetallic alloy.
TypeArticle
URIhttp://hdl.handle.net/1822/1568
DOI10.1023/A:1023948917115
ISSN0957-4530
Peer-Reviewedyes
AccessOpen access
Appears in Collections:CIICS - Artigos em revistas de circulação internacional com arbitragem científica
DEM - Artigos em revistas de circulação internacional com arbitragem científica

Files in This Item:
File Description SizeFormat 
JMS.pdf1,11 MBAdobe PDFView/Open

Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu ORCID